|Tolerances of 1mil are required for placement systems to ensure proper component positioning. |
Micro ball grid array packages (µBGA) rapidly are becoming the package of choice when designing new printed circuit board (PCB) assemblies. These packages generally offer high, first-pass process yields with significant real estate savings over their predecessors. Process or design errors occasionally require the need for rework. Because rework requires component removal, special considerations must be taken into account. These include excessive heat and improper removal as well as the fact that site-cleaning techniques have the potential to cause damage to component pads, adjacent components or the PCB itself. In short, proper rework requires sound practices, proper tools and quality training.
The list below provides advantages to using µBGA packages:
However, there are some disadvantages of the µBGA and LGA packages. First, solder joint is validated by X-ray inspection post reflow, which is time consuming and expensive. Second, the use of µBGAs involves a higher level of complexity in terms of signal trace routing on the PCB, which increases the cost of the board. Finally, despite the high first-pass yields of the µBGA and LGA, defective solder joints still occur for various reasons. As a result, the rework process becomes more involved because solder joints are hidden and cannot be touched up. The component must be completely removed from the board. This requires rework equipment, offering a higher level of process control.
Solder Paste or Flux Deposition
With lead-free µBGAs, solder balls melt at 217°C and typically contain adequate solder volume to create an acceptable joint. Current industry trends are to apply paste flux during the rework operation; this will reduce the need for custom solder paste plates and provide the necessary flux for proper attachment. This can be best accomplished with a flux dip plate that ensures a consistent application of paste flux to the bottom 30 percent of the solder ball.
|Array site with component removed. |
Conversely, LGAs require application of the correct thickness of solder paste, since the components are supplied tinned without adequate solder for connection to the PCB. In rework, solder paste is applied with a single component stencil directly to the bottom of the component. The part is then picked from the component nest on the rework machine without disturbing the deposition of the solder paste. During the rework of LGAs, solder paste volume is critical for long-term reliability. Stencil thickness and aperture sizes can be calculated for optimum solder volume. Consult manufacturers' data sheets to determine the appropriate paste volume needed for long-term reliability.
Featuring smaller ball sizes and finer pitches, µBGA and LGAs require more accurate placement. Typically, a machine with a placement accuracy of 1 mil is required. Likewise, the use of lead-free solders presents additional challenges, including decreased occurrences of self-centering during reflow and the inability to rely on the surface tension of the solder self-centering the device as in the past with standard, leaded BGAs.
The next significant concern associated with solder paste used in the LGA process is that of potential voids in solder joints caused by the flux material. Typically, these voids occur near the body of a LGA because the flux is lighter than the solder material, forcing it to rise to the top of the molten liquid ball. Therefore, it is helpful to inform the paste vendor that LGAs are involved in the process, ensuring that the proper formulation of solder paste or flux can be recommended. Obviously, the proper application of an appropriate reflow profile minimizes the possibility of voids. The reflow profile for LGA components is the same as for any surface mount device and the ideal reflow temperature is 235°C.
With µBGAs and LGAs, the nature of the defect types is quite similar to other SMT devices: solder bridging, cold solder joints or misalignment. In the case of defective joints, potential causes include defective solder balls, poor solder and/or flux quality, poor solder paste and/or flux deposition, unclean solder pads, or improperly applied reflow profiles. Misalignment, on the other hand, can be caused by a range of placement and handling problems.
Because the solder joints are inaccessible for single joint touchups and visual inspection, array devices often are the defect culprits on failed assemblies. Thus, it is critical that the rework process be carefully developed and performed with equipment that provides repeatable process control. The necessary rework process steps follow:
- Reflow (for removal)
- Site preparation
- Solder paste or flux deposition
Reflow:The application of a uniform, repeatable reflow profile is crucial. The heating process must cause the full array of solder joints to achieve reflow simultaneously, yet in such a way that does not sacrifice the integrity of the component, the board or any adjacent components. This is only achievable with a rework system that provides even heating on both the top and bottom sides of the board, with the heat flow contained within the space occupied by the device and applied in such a way that it minimizes any temperature gradients across the component. This calls for low-pressure convection airflow that heats through the body of the component. This should result in the simultaneous reflow of the joints that, combined with automatic vacuum part removal, reduces the probability of lifting pads off the board.
For each combination of PCB and array component, an appropriate reflow profile must be established. Careful profile setup is the key to successful reflow, and the proper placement of thermocouples during testing is critical to ensure uniform temperature across the component and the PCB assembly. Board profiling must be done on a completely populated PCB with new thermocouples, a calibrated recording device and placement of the thermocouples in both high and low thermal demand areas of the board. The rework equipment should allow the operator to monitor temperatures beneath the component body as well as the output temperatures of the system's heaters.
Site preparation: After component removal, the pads need to be prepared for the replacement component. The residual solder should be removed with a solder wick saturated with paste flux, used in conjunction with a direct power soldering iron equipped with a hot blade tip. The operator must be careful, keeping the wick between the tip and the board. The old solder can be removed quickly without risking pad damage that is likely to result from direct contact between a hot tip and the board. Subsequently, flux residue on the board should be removed with an approved solvent, leaving the land area clean and ready for the solder paste or flux application.
Solder paste or flux deposition: In the case of LGAs, it is necessary to deposit solder paste on the pads in preparation for reflow of the replacement component. The deposition of the paste or flux can be achieved by using a single-component stencil plate. This allows for deposition on the bottom of the component without worry of adjacent components; such a product can be used with standard assembly solder paste.
Placement: The placement of ?BGAs and LGAs in the rework process requires the simultaneous viewing of pads and leads at an adequately high magnification (i.e., 30-50X). Once the images of the pads and leads have been aligned, the component is placed onto the board. For most LGAs, viewing at 25X magnification should be sufficient; however, 50X magnification is required with µBGAs because of the smaller size of these packages to ensure that the balls and pads are properly registered and aligned.
Reflow: As previously mentioned, it is critical to apply a uniform, repeatable reflow profile. Profile setup is the key to successful reflow, and the proper placement of thermocouples during testing ensures uniform temperature across the component and the PCB assembly.
The rework equipment must provide all the necessary functions described in the rework process (see above). The level of process control is especially critical in the reflow procedure, whether in the removal or replacement mode; although improper site cleaning, solder paste deposition and component placement can be corrected by repeating the process. Poor process control in reflow can destroy the component, adjacent components or the board.
| Micro array rework requires the right tools.|
The equipment should offer the appropriate balance between the level of process control provided and the ease and simplicity of equipment operation. A graphical interface enables the operator to visualize the temperature parameters during rework and save the actual process graph for verification and future analysis. Additionally, it is important that operators and technicians be properly trained and have the equipment available to properly identify any defective components.
All the factors that make the µBGA package more attractive than peripheral-leaded devices in the assembly environment carry through to rework. For example, the ease of solder or flux deposition on a µBGA pad pattern and the ease of alignment and placement of µBGAs with image overlay technology makes µBGA rework easier in comparison to fine-pitch QFPs. With the introduction of high-quality, lower-priced convection array rework systems, users have the benefits of an easy-to-use system combined with the technology and process control to ensure repeatable results.
Contact: OK International, Inc., 12151 Monarch Street, Garden Grove, CA 92841, 1-714-799-9910 fax: 1-714-799-9533 Web: http://www.okinternational.com email@example.com